Ceramic Fiber
Made by double-sided needle punching, it improves fiber entanglement and delamination resistance.
Low thermal conductivity, good thermal insulation performance, and low shrinkage at high temperatures.
Low bulk density and low heat capacity, significantly shortening the heating and cooling time of the furnace.
Good tensile strength.
Good chemical stability and corrosion resistance.
Good thermal shock resistance and sound absorption performance.
Easy to cut and install.
| Ceramic Fiber Blankets | ||||||
| Brand | ST -1260 | GC -1260 | HA -1360 | HZ-1430 | PC-1600 | |
| Specification Temp. (℃) | 1260 | 1260 | 1360 | 1430 | 1600 | |
| Working Temp. (℃) | 1050 | 1100 | 1200 | 1350 | 1500 | |
| Bulk Density (kg/m3) | 64-160 | 64-160 | 64-160 | 64-160 | 96/128 | |
| @24H | -3 | -3 | -3 | -3 | -1 | |
| Linear Shrinkage after Heating | (1000℃) | (1100℃) | (1250℃) | (1350℃) | (1400℃) | |
| (w/m.k) Thermal Conductivity | 0.09(400℃) | 0.09(400℃) | 0.09(400℃) | 0.09(400℃) | 0.16(600℃) | |
| 0.17(800℃) | 0.17(800℃) | 0.13(600℃) | 0.76(600℃) | 0.28(1000℃) | ||
| 0.32(1000℃) | 0.31(1000℃) | 0.22(1000℃) | 0.22(1000℃) | 0.45(1400℃) | ||
| Tensile strength (MPa) | 0.05 | 0.05 | 0.06 | 0.06 | 0.08 | |
| (%) | Al2O3 | 43 | 44 | 51 | 35 | 71 |
| Chemical Composition | Al2O3+SiO2 | 96 | 98 | 99 | – | – |
| ZrO2 | – | – | – | 13-15 | – | |
| Fe2O3 | 1 | 0.5 | 0.2 | 0.2 | 0.2 | |
| Na2O+K2O | 0.5 | 0.3 | 0.2 | 0.2 | 0.2 | |
| Size(mm) | LENGTH*WIDTH*THICKNESS | THICKNESS | ||||
| 7200*610/1220*25，3600*610/1220*50，4800*610/1220*38 | from 10-25 | |||||
| 7200*610/1220*6，14400*610/1220*12.5，28800*610/1220*6.38 | ||||||